测试高温条件(90、130、170和190℃)下以聚苯硫醚(PPS)为基布和以聚四氟乙烯(PTFE)为基布的PPS针刺过滤毡的拉伸性能，并与其常温下的拉伸性能进行对比。结果表明，高温条件下2种基布针刺毡的经纬向断裂强力均出现不同程度的下降；PTFE基布针刺毡在190℃下的纬向断裂强力仅为常温下的20%;所有PPS针刺过滤毡试样的定负荷伸长率均随着测试温度的升高而增加。
Abstract：Tensile properties of two types of polyphenylene sulfide(PPS)needle punched filter felts with PPS scrim and polytetrafluoroethylene(PTFE)scrim at high temperature(90, 130, 170 and 190 ℃) were tested and compared with those at normal temperature. It was found that at high temperature, the warp and weft breaking strength of the two types of needle punched felts decreased to varying degrees. The weft breaking strength of the felt with PTFE scrim at 190 ℃ was only 20% of that at normal temperature. And elongation under constant load for all the PPS needle punched felt samples increased with the increase of test temperature.
[1] 王玉红，姚群，陈志炜.我国袋式除尘行业技术新进展[J].工业安全与环保，2020,46(6):65-70.
[2] 赵奕，靳向煜，吴海波，等.我国高温烟气非织造过滤材料的现状与发展前景[J].东华大学学报(自然科学版),2020,46(6):874-880.
[3] 郭乃盐，赵霞.除尘滤袋失效在线检测分析系统的研发[J].国际纺织导报，2021,49(7):28-31.
[4] 柳静献，毛宁，常德强，等.温度对PPS针刺毡滤料的影响研究[C]//2008(沈阳)国际安全科学与技术学术研讨会论文集.沈阳，2008.
[5] 王向钦，陈明刚，吴波伟，等.除尘滤袋用PTFE复合缝纫线热态拉伸性能分析[J].产业用纺织品，2021,39(12):15-18.
[6] 毛宁，高洋，韩旭，等.袋式除尘用滤料挺度与温度关系的试验研究[J].安全与环境学报，2023,23(3):826-829.
[7] 严烁，梁燕，周蕊，等.袋式除尘器用聚苯硫醚滤料的拉伸强度及失效演化[J].合成纤维，2022,51(3):20-24.
[8] 彭杰，任捷，崔宁.PPS针刺过滤毡常温下拉伸特点研究[J].产业用纺织品，2020,38(2):22-27.
[9] 郑依铭，吴海波.聚四氟乙烯滤料的高温蠕变行为与抗蠕变研究[J].毛纺科技，2022,50(1):1-6.
[10] 雷李娜，郭国梁.国内袋式除尘器滤袋滤料标准研究与质量问题分析[J].产业用纺织品，2023,41(11):42-45.
[11] ZHENG C H,KANAOKA C.Recent advances in dust collection technology and ISO standardization in bag filtration[J].Journal of Zhejiang University:Science A,2018,19(1):21-33.
基本信息:
DOI：
中图分类号:TS101.923
引用信息:
[1]崔宁,李亚儒,施永明.PPS针刺过滤毡的热态拉伸性能[J].产业用纺织品,2024,42(12):14-19.
基金信息: